Apparatus for manufacturing polysilicon based electron-beam melting using dummy bar and method of manufacturing polysilicon using the same

ABSTRACT

Methods and apparatus for manufacturing high purity polysilicon. The apparatus includes a vacuum chamber; first and second electron guns disposed at an upper side of the vacuum chamber to irradiate electron beams into the vacuum chamber; a silicon melting unit which is placed on a first electron beam-irradiating region corresponding to the first electron gun and to which powdery raw silicon is fed and melted by the first electron beam; and a unidirectional solidification unit placed on a second electron beam-irradiating region corresponding to the second electron gun. The unidirectional solidification unit is provided therein with a start block driven in a downward direction to transfer molten silicon in the downward direction and is formed at a lower side thereof with a cooling channel. The start block includes a dummy bar having a silicon button joined to an upper portion of the dummy bar.

BACKGROUND

1. Technical Field

The present invention relates to a technique for manufacturing polysilicon, and more particularly, to a method and apparatus for manufacturing polysilicon based on electron-beam melting using a dummy bar to improve silicon refining efficiency.

2. Description of the Related Art

Purity of silicon is typically represented by 2N, 3N, 6N, 11N, and the like. Here, the numeral in front of ‘N’ means the number of nines (9) in percent by weight (wt %). For example, 2N means a purity of 99%, 6N means a purity of 99.9999%, and 11N means a purity of 99.999999999%.

Semiconductor level silicon requires an ultra-high purity approaching 11N. However, as known in the art, silicon used as a raw material for photovoltaic cells and having a relatively low purity of 5N to 7N provides similar optical conversion efficiency to silicon having a high purity of 11N.

Semiconductor level silicon is produced through chemical gasification processes. However, such a silicon production process generates a large amount of contaminants, and has low production efficiency in spite of high production cost.

Thus, the silicon production process is not suited to production of semiconductor level silicon used as a raw material for photovoltaic cells, and efforts for developing metallurgical refining processes capable of achieving mass production of high purity silicon at low cost have been actively attempted.

Examples of metallurgical refining processes for production of high purity silicon for photovoltaic cells include a vacuum refining process, a wet refining process, an oxidation process, a unidirectional solidification refining process, and the like. Some of these refining processes are commercially used in the art.

Particularly, silicon manufacturing techniques based on metal melting such as vacuum refining and unidirectional solidification refining have been actively studied due to merits thereof, such as easy characteristic control and less contamination due to impurities during operation.

Here, the vacuum refining process is a process in which a raw metal is melted and impurities having lower boiling point and vapor pressure than silicon are removed from the molten metal, and the unidirectional solidification refining process is a process in which impurities are moved (segregated) along an interface between solid and liquid during phase change of silicon from liquid to solid.

BRIEF SUMMARY

The present invention provides an apparatus for manufacturing high purity polysilicon based on electron-beam melting using a dummy bar to improve silicon refining efficiency.

The present invention also provides a method of manufacturing high purity polysilicon based on electron-beam melting using a dummy bar, which can maximize efficiency of removing metal impurities through control of the dummy bar.

In accordance with one aspect of the present invention, an apparatus for manufacturing polysilicon includes: a vacuum chamber; first and second electron guns disposed at an upper side of the vacuum chamber to irradiate electron beams into the vacuum chamber; a silicon melting unit which is placed on a first electron beam-irradiating region corresponding to the first electron gun and to which powdery raw silicon is fed and melted by the first electron beam; and a unidirectional solidification unit placed on a second electron beam-irradiating region corresponding to the second electron gun, the unidirectional solidification unit being provided therein with a start block which is driven in a downward direction to transfer molten silicon in the downward direction and being formed at a lower part thereof with a cooling channel such that the molten silicon is solidified and cast from a lower portion thereof to an upper portion thereof, the start block comprising a dummy bar which has a silicon button joined to an upper portion of the dummy bar.

In accordance with another aspect of the present invention, a method of manufacturing polysilicon includes: feeding powdery raw silicon to a silicon melting unit and melting the fed raw silicon by irradiating electron beam upon the raw silicon; continuously feeding and melting the raw silicon such that molten silicon is overflowed from the silicon melting unit; receiving, by an unidirectional solidification unit, the molten silicon overflowed from the silicon melting unit, transferring the molten silicon in a downward direction by driving a start block with silicon material, followed by solidifing the molten silicon from a lower portion thereof to an upper portion thereof to form a refined silicon ingot; and cutting off an upper portion of the refined silicon ingot to remove metal impurities from the silicon ingot.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other aspects, features, and advantages of the invention will become apparent from the detailed description of the following embodiments in conjunction with the accompanying drawings:

FIG. 1 is a schematic view of an apparatus for manufacturing polysilicon based on electron-beam melting in accordance with one embodiment of the present invention;

FIG. 2 is a sectional view of a start block including a dummy bar in accordance with one embodiment of the present invention;

FIG. 3 is a flowchart of a method of manufacturing polysilicon in accordance with one embodiment of the present invention;

FIG. 4 shows one example of a solid/liquid interface formed by an electron beam pattern applicable to the present invention;

FIG. 5 is a cross-section of a cast polysilicon ingot prepared through application of a start block having a graphite dummy bar joined to a silicon button;

FIG. 6 is a cross-section of a cast polysilicon ingot prepared through application of a start block having a graphite dummy bar without a silicon button;

FIG. 7 is a picture of a polysilicon ingot prepared according to one example of the present invention; and

FIG. 8 is a picture of a cross-section near an impurity boundary of the polysilicon ingot prepared according to the one example of the present invention.

DETAILED DESCRIPTION

Embodiments of the invention will now be described in detail with reference to the accompanying drawings. It should be understood that the present invention is not limited to the following embodiments and may be embodied in different ways, and that the embodiments are given to provide complete disclosure of the invention and to provide thorough understanding of the invention to those skilled in the art. The scope of the invention is limited only by the accompanying claims and equivalents thereof. Like components will be denoted by like reference numerals throughout the specification.

Next, an apparatus and method for manufacturing polysilicon based on electron-beam melting using a dummy bar according to embodiments of the invention will be described with reference to the accompanying drawings.

FIG. 1 is a schematic view of an apparatus for manufacturing polysilicon based on electron-beam melting in accordance with one embodiment of the present invention.

Referring to FIG. 1, the polysilicon manufacturing apparatus includes a vacuum chamber 110, two electron guns including a first electron gun 120 a and a second electron gun 120 b, a silicon melting unit 130, and a unidirectional solidification unit 140.

The vacuum chamber 110 is maintained at a high vacuum of 10-4 Torr during melting of raw silicon and casting of molten silicon. The internal pressure of the vacuum chamber 110 may be maintained at 10-5 Torr.

The first and second electron guns 120 a, 120 b are placed at an upper side of the vacuum chamber 110 to irradiate electron beams into the vacuum chamber 110.

The silicon melting unit 130 is placed on a region to which a first electron beam is irradiated from the first electron gun 120 a, that is, a first electron beam-irradiating region. Raw silicon powder is fed from a raw silicon supply unit 101 into the silicon melting unit 130, and is then melted by a first electron beam accelerated and accumulated by the first electron gun 120 a.

Here, the first electron gun 120 a may accelerate and accumulate the first electron beam to achieve an output energy of 4000 kW/m2 or less, for example, about 2000 to 4000 kW/m2 such that molten silicon does not exhibit unstable behavior like spattering out of a crucible.

The silicon melting unit 130 may be provided with a water-cooling type crucible, which is capable of facilitating control of cooling efficiency. The water-cooling type crucible may have a cooling channel which can be filled with a fluid at a surface of the crucible.

A material of the water-cooling type crucible may be copper (Cu) such that a molten silicon is not contaminated by an original material of the silicon melting unit 130 while a silicon is refined.

The unidirectional solidification unit 140 enables continuous casting of the molten silicon while inducing segregation of metal impurities, thereby enhancing silicon refining efficiency in production of high purity polysilicon. The unidirectional solidification unit 140 is placed on a region to which a second electron beam is irradiated from the second electron gun 120 b, that is, a second electron beam-irradiating region, and is connected to the silicon melting unit 130 via a runner 135. The runner 35 may be attached to the silicon melting unit 130 or the unidirectional solidification unit 140. As the raw silicon is continuously fed into the silicon melting unit 130, the amount of molten silicon within the silicon melting unit 130 increases. Accordingly, the molten silicon overflowed from the silicon melting unit 130 is supplied into the unidirectional solidification unit 140 via the runner 135.

Further, the unidirectional solidification unit 140 is formed at a lower part thereof with a cooling channel 142 through which cooling water or the like is supplied to cool the molten silicon. Thus, a solidification efficiency of the molten silicon is improved. Further, the unidirectional solidification unit 140 is provided therein with a start block 145 which is driven in a downward direction.

The start block 145 is driven in the downward direction within the unidirectional solidification unit 140 to transfer the molten silicon in the downward direction while growing a cast for silicon casting.

The start block 145 may include a dummy bar to which a high purity silicon button is joined to prevent a cast silicon ingot from being contaminated by graphite.

In the unidirectional solidification unit 140, the molten silicon fed from the silicon melting unit 130 is transferred towards the cooling channel 142 by the start block 145 while being kept in a molten state by a second electron beam accelerated and accumulated by the second electron gun 120 a, and is then solidified and cast in an upward direction through by a fluid filled into the cooling channel 142.

The second electron gun 120 b may accelerate and accumulate the second electron beam to achieve an output energy of 1000 to 2000 kW/m2 such that the silicon is able to maintain in a molten state and the molten silicon does not exhibits unstable behavior like spattering out of the crucible. Because such unstable behavior of the molten silicon affects overflow of the molten silicon from the melting unit.

The unidirectional solidification unit 140 may include a copper casting container, which is formed at a lower part thereof with a cooling channel, as in the water cooling type crucible.

FIG. 2 is a sectional view of a start block including a dummy bar according to one embodiment of the present invention.

Referring to FIG. 2, the start block 145 may includes a high purity silicon button 147 joined to an upper side of a dummy bar 146.

The silicon button 147 may have a purity of 8N to 10N and a thickness of about 10 to 15 mm, and is formed when a silicon chunk is melted by the second electron beam and joined to the dummy bar 146 within the unidirectional solidification unit 140.

The dummy bar 146 may be made of a graphite material.

Specifically, the dummy bar 146 may be made of low density graphite and have a porous surface thereof. The graphite dummy bar 146 allows silicon molten by the second electron beam to be strongly joined to the dummy bar after infiltrating into and being solidified inside a porous surface of the graphite dummy bar. Thus it may prevent rapid variation in temperature between the lower cooling channel and the initial molten silicon. Here, when the silicon block 145 is constituted only by the dummy bar 146 instead of the combination of the dummy bar and the start block, a cast silicon ingot can be contaminated by graphite of the dummy bar.

Thus, the silicon button 147 prevents the dummy bar 136 from coming into direct contact with the molten silicon or cast silicon ingot, thereby preventing the molten silicon or cast silicon from being contaminated by graphite of the dummy bar 145

FIG. 3 is a flowchart of a method of manufacturing polysilicon in accordance with one embodiment of the present invention

Referring to FIG. 3, the method of manufacturing polysilicon according to this embodiment includes preparing a polysilicon manufacturing apparatus in S310, mounting a dummy bar in S320, preparing a start block by melting a silicon button in S330, feeding and melting low purity silicon in S340, overflowing molten silicon in S350, refining through solidification of molten silicon in S360, and cutting off an upper portion of a cast silicon ingot in S370.

In operation S310 of preparing a polysilicon manufacturing apparatus, the apparatus including a vacuum chamber, first and second electron guns, a silicon melting unit, and a unidirectional solidification unit as shown in FIG. 1, is prepared to melt raw silicon and cast molten silicon.

In operation S320 of mounting a dummy bar, the dummy bar is mounted within the unidirectional solidification unit. Then, in operation S330 of preparing a start block, the start block is prepared by melting a silicon button on the dummy bar.

Mounting of the dummy bar may be performed by the following process.

First, a dummy bar made of graphite or the like is mounted inside the unidirectional solidification unit. Then, a silicon chunk is placed on the dummy bar. Next, the silicon chunk is melted by a second electron beam to be joined to the dummy bar under a vacuum atmosphere of about 10-5 Torr. Through this process, a start block having the silicon button placed at an upper portion of the start block and joined to the dummy bar placed at a lower portion thereof is formed.

Then, in operation S340 of feeding and melting low purity silicon, powdery raw silicon is fed to the silicon melting unit, and a first electron beam is irradiated upon the raw silicon from the first electron gun to melt the raw silicon. The powdery raw silicon may have a purity of 2N and a mean particle diameter of 1 to 2 mm.

While the raw silicon is melted by the first electron beam, volatile components, such as aluminum (Al), calcium (Ca), phosphorous (P), magnesium (Mg), and manganese (Mn), are removed from the raw silicon via vacuum volatilization.

Volatile impurities having lower boiling point and vapor pressure than silicon are volatilized at high temperature generated by the first electron beam under high vacuum. Here, refining efficiency may be enhanced by increasing the output energy and irradiation time of the first electron beam.

In operation S340, the first electron beam may be accelerated and accumulated by the first electron gun to achieve an output energy of about 4000 kW/m2, thereby facilitating silicon melting and removal of volatile impurities.

Next, in operation S350 of overflowing the molten silicon, the raw silicon is continuously fed to the silicon melting unit, and thus the amount of molten silicon in the silicon melting unit continues to increase, so that the molten silicon overflows from the silicon melting unit and is supplied to the unidirectional solidification unit through the runner.

Next, in operation S360 of refining the molten silicon through solidification of the molten silicon, the unidirectional solidification unit receives the molten silicon and transfers the molten silicon in a downward direction by driving the start block including the dummy bar in the downward direction, while keeping the silicon in a molten state by irradiating a second electron beam from the second electron gun upon the molten silicon. Then, the molten silicon is solidified from a lower portion thereof simultaneously with refining of the molten silicon from the lower portion thereof to an upper portion thereof, thereby providing a cast silicon ingot.

In operation S360, the second electron beam may be accelerated and accumulated by the second electron gun to achieve an output energy of about 1000 to 2000 kW/m2 in order to maintain the silicon in a molten state while being supplied from the silicon melting unit.

In operation S360, the start block may be driven to descend at a rate of 0.005 to 0.05 mm/s to achieve process control as well as to prohibit the molten silicon from leaking below the unidirectional solidification unit.

In this process, iron (Fe), nickel (Ni), titanium (Ni), chromium (Cr), copper (Cu) and the like contained in the molten silicon move upwards along a solid/liquid interface. Such an effect of segregating the impurities may be sufficiently exhibited when temperature difference between a liquid phase 420 and a solid phase 410 is high while the solid/liquid interface is maintained to be vertical to the growth direction during solidification of the molten silicon, as shown in FIG. 4.

According to this embodiment, the unidirectional solidification unit is provided with the start block including the dummy bar, so that the silicon is maintained in a molten state for a relatively long period of time by the second electron beam and behavior of the molten silicon can be easily controlled through the start block including the dummy bar, thereby enhancing efficiency of impurity segregation along the solid/liquid interface.

Next, in operation S370 of cutting off an upper portion of the silicon ingot, the upper portion of the cast silicon ingot is cut off. As the impurities contained in the molten silicon move upwards along the solid/liquid interface, segregation of the metal impurities is concentrated at the uppermost portion of the cast silicon ingot (see FIG. 8). Accordingly, it is possible to provide high purity polysilicon by removing the uppermost portion of the cast silicon ingot.

According to this embodiment, the final polysilicon may have a diameter of about 100 mm and a height of 1 to 1000 mm through adjustment of operation time and growth speed. Here, the process is controlled such that the upper portion of the cast silicon where the impurities are concentrated is less than 20% of the overall height of the sample.

The polysilicon produced through this process may have a purity of 5N to 7N and thus may be applied to photovoltaic cells.

As such, according to the embodiments, the method and apparatus for manufacturing polysilicon based on electron-beam melting using a dummy bar may achieve removal of volatile impurities via vacuum refining using a first electron beam.

Further, the polysilicon manufacturing apparatus according to the embodiments may easily control behavior of molten silicon through application of a dummy bar during unidirectional solidification of the molten silicon, thereby enhancing efficiency in removal of metal impurities.

The polysilicon prepared by the method according to the embodiment has a purity of 5N to 7N and thus may be used for photovoltaic cells.

Example

Next, the constitution and functions of the present invention will be explained in more detail with reference to the following examples. These examples are provided for illustrative purposes only and are not to be in any way construed as limiting the invention.

A description of details apparent to those skilled in the art will be omitted herein.

First, polysilicon was produced by the following process.

A graphite dummy bar was mounted inside the unidirectional solidification unit and a silicon chunk having a purity of 9N and a weight of 180 g was fed thereto. Then, with the vacuum chamber maintained under a high vacuum of 10-5 Torr, an electron beam was irradiated from the second electron gun to the silicon at an output energy of 2000 kW/m2 for 10 minutes to melt the raw silicon, and the molten silicon was joined to the dummy bar under the molten silicon.

Silicon powder having a particle size of 1 to 10 mm and fed to the water cooling type crucible through the raw supply apparatus was supplied to the silicon melting unit, and, at the same time, a first electron beam was irradiated to the silicon powder at an output energy of 1000 to 1500 kW/m2 in a pattern shown in FIG. 5 using the first electron gun.

Then, the molten silicon was supplied to the unidirectional solidification unit along the runner, and the start block was lowered at a rate of 0.005 to 0.05 mm/s and cooled while irradiating a second electron beam having an output energy of 1000 to 2000 kW/m2 to the molten silicon in a complex circular pattern as shown in FIG. 6 using the second electron gun so as to maintain the silicon in a molten state.

FIG. 5 is a cross-section of a cast polysilicon ingot prepared through application of a start block having a graphite dummy bar joined to a silicon button, and FIG. 6 is a cross-section of a cast polysilicon ingot prepared through application of a start block having a graphite dummy bar without a silicon button.

As shown in FIG. 5, a graphite contamination does not appear in the polysilicon layer 450 of the cast polysilicon ingot, whereas in accordance with FIG. 6, a graphite contamination 450 a appears in the polysilicon layer 450 of the cast polysilicon ingot. That is, it can be seen that the cast polysilicon ingot prepared through application of a start block having a graphite dummy bar joined to a silicon button exhibits a much lower degree of graphite contamination than the cast polysilicon ingot prepared through application of a start block having a graphite dummy bar without a silicon button.

FIG. 7 is a picture of a polysilicon ingot prepared according to one example of the invention, and FIG. 8 is a picture of a cross-section near an impurity boundary of the polysilicon ingot prepared according to the one example of the invention.

Referring to FIGS. 7 and 8, it can be seen that metal impurities 401 were moved towards the uppermost portion of an ingot 400 during manufacture of polysilicon.

Table 1 shows analysis results of purity of an impurity layer and a refining layer through ICP-AES analysis of polysilicon prepared according to the example.

TABLE 1 (unit: ppm) Al Ca Fe Ti Cu Mn Ni P Purity % Raw Silicon 446 148 831 85.9 <10 158 <10 200 98.11 Impurity layer 2046 <10 22490 1696 43532 190 1672 <1 92.84 Refining layer not not not not not not not not ~99.9999 detected detected detected detected detected detected detected detected

Referring to Table 1, it can be seen that the raw silicon having a purity of 2N was refined to a purity of 6N and the impurities were concentrated in the impurity layer at the uppermost portion of the polysilicon ingot produced using the apparatus according to the present invention.

Although some embodiments have been described herein, it should be understood by those skilled in the art that these embodiments are given by way of illustration only, and that various modifications, variations, and alterations can be made without departing from the spirit and scope of the invention. Therefore, the scope of the invention should be limited only by the accompanying claims and equivalents thereof. 

What is claimed is:
 1. An apparatus for manufacturing polysilicon, comprising: a vacuum chamber; first and second electron guns disposed at an upper side of the vacuum chamber to irradiate electron beams into the vacuum chamber; a silicon melting unit which is placed on a first electron beam-irradiating region corresponding to the first electron gun and to which powdery raw silicon is fed and melted by the first electron beam; and a unidirectional solidification unit placed on a second electron beam-irradiating region corresponding to the second electron gun, the unidirectional solidification unit being provided therein with a start block which is driven in a downward direction to transfer molten silicon in the downward direction and being formed at a lower part thereof with a cooling channel such that the molten silicon is solidified and cast from a lower portion thereof to an upper portion thereof, the start block comprising a dummy bar which has a silicon button joined to an upper portion of the dummy bar.
 2. The apparatus of claim 1, wherein the dummy bar is made of graphite.
 3. The apparatus of claim 1, wherein a surface of the dummy bar which is joined to the silicon button is a porous surface.
 4. The apparatus of claim 1, wherein the unidirectional solidification unit is provided with a casting container, the casting container being made of copper and formed at a lower side thereof with a cooling channel.
 5. The apparatus of claim 1, wherein the silicon button has a purity of 8N to 10N, and a thickness of 10 to 15 mm.
 6. The apparatus of claim 1, wherein the silicon button is formed by melting a silicon chunk within the unidirectional solidification unit to be melt and joined to the dummy bar.
 7. An apparatus for manufacturing polysilicon, comprising: an electron gun; a silicon melting unit which is filled with a silicon melted by the electron gun; and a unidirectional solidification unit that receives a molten silicon from the silicon melting unit, include a start block therein which allows the molten silicon to transfer in a downward direction of the unidirectional solidification unit, wherein the start block includes a silicon button faced to the molten silicon and a dummy bar joined to the silicon button.
 8. The apparatus of claim 7, wherein a purity of the silicon button is higher than that of the molten silicon.
 9. The apparatus of claim 7, wherein the dummy bar has a porous surface.
 10. A method of manufacturing polysilicon comprising: feeding powdery raw silicon to a silicon melting unit and melting the fed raw silicon by irradiating electron beam upon the raw silicon; continuously feeding and melting the raw silicon such that molten silicon is overflowed from the silicon melting unit; receiving, by an unidirectional solidification unit, the molten silicon overflowed from the silicon melting unit, transferring the molten silicon in a downward direction by driving a start block with silicon material, followed by solidifying the molten silicon from a lower portion thereof to an upper portion thereof to form a refined silicon ingot; and cutting off an upper portion of the refined silicon ingot to remove metal impurities from the silicon ingot.
 11. The method of claim 10, wherein the start block is lowered at a rate of 0.0005 to 0.05 mm/s.
 12. The method of claim 10, wherein the raw silicon has a purity of 2N and a mean particle diameter of 1 to 2 mm.
 13. The method of claim 10, wherein, when melting the fed raw silicon, volatile impurities are volatilized from the raw silicon under vacuum.
 14. The method of claim 13, wherein metal impurities contained in the molten silicon are moved to the upper portion of the molten silicon along a solid/liquid interface during solidification of the molten silicon. 